PB826G3
Release Date: 30/11/2012
15% Glass Fiber Reinforced, Impact Modified and UV Stabilizied Polyamide 6 for Injection Moulding applications.
| ISO |
|
ASTM |
|
RELATED
DOCUMENTS |
|
| PHYSICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| DENSITY |
g/m3 |
ISO-1183 |
1.18 |
| WATER ABSORPTION (SATURATION) |
% |
ISO-62 |
7.3 |
MOISTURE ABSORPTION
23° C, 50% RH (SATURATION) |
% |
ISO-62 |
2.5 |
| MOULD SHRINKAGE |
% |
ISO-2577 |
0.4-0.7 |
| MECHANICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| TENSILE YIELD STRENGTH |
MPa |
ISO-527 |
100 |
| TENSILE MODULUS |
MPa |
ISO-527 |
4900 |
| STRAIN @ BREAK |
% |
ISO-527 |
3.5 |
| FLEXURAL STRENGTH |
MPa |
ISO-178 |
140 |
| FLEXURAL MODULUS |
MPa |
ISO-178 |
4500 |
| NOTCHED IZOD IMPACT STRENGTH +23°C |
Kj/m2 |
ISO-180 |
15 |
| NOTCHED CHARPY IMPACT STRENGTH +23°C |
Kj/m2 |
ISO-179 |
20 |
| NOTCHED CHARPY IMPACT STRENGTH -30°C |
Kj/m2 |
ISO-179 |
8 |
| UN NOTCHED CHARPY IMPACT STRENGTH +23°C |
Kj/m2 |
ISO-179 |
72 |
| UN NOTCHED CHARPY IMPACT STRENGTH -30°C |
Kj/m2 |
ISO-179 |
70 |
| ROCKWELL HARDNESS |
|
R scale |
85 |
| THERMAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| HDT AT LOAD 1.8 Mpa |
°C |
ISO-75 |
170 |
| HDT AT LOAD 0.45 Mpa |
°C |
ISO-75 |
210 |
| VICAT SOFTENING POINT |
°C |
ISO-306 |
215 |
| FLAMMABILITY |
mm/min |
FMVSS302 |
20 |
| UL FLAMMABILITY |
|
UL-94 3mm |
H.B. |
| MELTING POINT |
°C |
ISO-11357 |
218 |
| MAX TEMP CONTINUOUS USE |
°C |
|
110 |
MAX TEMP SHORT
PEAKS OPERATION |
°C |
|
200 |
| ELECTRICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| SURFACE RESISTANCE |
Ohm |
IEC 60093 |
10^10 |
| VOLUME RESISTANCE |
Ohm x m |
IEC 60093 |
10^10 |
| DIELECTRIC STRENGTH |
kV/mm |
IEC 60250 |
80 |
| PHYSICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| DENSITY |
g/m3< |
ASTM-D792 |
1.18 |
| WATER ABSORPTION (SATURATION) |
% |
ASTM-D570 |
7.3 |
| MOULD SHRINKAGE |
% |
-- |
0.4-0.7 |
MOISTURE ABSORPTION
23° C, 50% RH (SATURATION) |
% |
ASTM-D570 |
2.5 |
| MECHANICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| TENSILE YIELD STRENGTH |
MPa |
ASTM-D638 |
100 |
| TENSILE MODULUS |
MPa |
ASTM-D790 |
4900 |
| STRAIN @ BREAK |
% |
ASTM-D638 |
3.5 |
| FLEXURAL STRENGTH |
MPa |
ASTM-D790 |
140 |
| FLEXURAL MODULUS |
MPa |
ASTM-D790 |
4500 |
| NOTCHED IZOD IMPACT STRENGTH +23°C |
j/m |
ASTM-D256 |
140 |
| THERMAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| HDT AT LOAD 1.8 Mpa |
°C |
ASTM D-648 |
170 |
| HDT AT LOAD 0.45 Mpa |
°C |
ASTM D-648 |
210 |
| VICAT SOFTENING POINT |
°C |
ASTM-D1525 |
215 |
| FLAMMABILITY |
mm/min |
FMVSS302 |
20 |
| UL FLAMMABILITY |
-- |
UL 94 3mm |
H.B. |
| MELTING POINT |
°C |
ASTM-D3417 |
218 |
| MAX TEMP CONTINUOUS USE |
°C |
|
110 |
MAX TEMP SHORT
PEAKS OPERATION |
°C |
|
200 |
| ELECTRICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| SURFACE RESISTANCE |
Ohm |
IEC 60093 |
10^10 |
| VOLUME RESISTANCE |
Ohmxcm |
IEC 60093 |
10^10 |
| DIELECTRIC STRENGTH |
kV/mm |
IEC 60250 |
80 |
|
The information contained in this website is supplied in good faith. However, it is given purely as an indication. It shall not be construed in any way as formal commitment or warranty on our part. Notably in respect of the eventual infringement of any rights of third parties who may use our products. We remain at your entire disposal for any further information that you may require.