PF300G6
Release Date: 10/08/2011
30% Glass Fiber Reinforced PBT for Injection Moulding applications.
| ISO |
|
ASTM |
|
RELATED
DOCUMENTS |
|
| PHYSICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| DENSITY |
g/cm3 |
ISO-1183 |
1.53 |
| WATER ABSORPTION (SATURATION) |
% |
ISO-62 |
0.5 |
MOISTURE ABSORPTION
23° C, 50% RH (SATURATION) |
% |
ISO-62 |
0.1 |
| MOULD SHRINKAGE |
% |
ISO-2577 |
0.3 |
| MFI |
g/10min |
ISO-1133 250/2.16 |
15 |
| MECHANICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| TENSILE YIELD STRENGTH |
MPa |
ISO-527 |
140 |
| TENSILE MODULUS |
MPa |
ISO-527 |
9000 |
| STRAIN @ BREAK |
% |
ISO-527 |
3 |
| FLEXURAL STRENGTH |
MPa |
ISO-178 |
180 |
| FLEXURAL MODULUS |
MPa |
ISO-178 |
8000 |
| NOTCHED IZOD IMPACT STRENGTH +23°C |
Kj/m2 |
ISO-180 |
12.5 |
| NOTCHED IZOD IMPACT STRENGTH -30°C |
Kj/m2 |
ISO-180 |
8.5 |
| NOTCHED CHARPY IMPACT STRENGTH +23°C |
Kj/m2 |
ISO-179 |
12 |
| NOTCHED CHARPY IMPACT STRENGTH -30°C |
Kj/m2 |
ISO-179 |
9 |
| UN NOTCHED CHARPY IMPACT STRENGTH +23°C |
Kj/m2 |
ISO-179 |
65 |
| UN NOTCHED CHARPY IMPACT STRENGTH -30°C |
Kj/m2 |
ISO-179 |
60 |
| THERMAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| HDT AT LOAD 1.8 Mpa |
°C |
ISO-75 |
210 |
| HDT AT LOAD 0.45 Mpa |
°C |
ISO-75 |
220 |
| G.W.F.I |
°C |
IEC 60695 |
650 |
| G.W.I.T. |
°C |
IEC 60695 |
675 |
| FLAMMABILITY |
mm/min |
FMVSS302 |
10 |
| UL FLAMMABILITY |
|
UL-94 3mm |
H.B. |
| MELTING POINT |
°C |
ISO-11357 |
226 |
| ELECTRICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| VOLUME RESISTANCE |
Ohm x m |
IEC 60093 |
10^15 |
| DIELECTRIC STRENGTH |
kV/mm |
IEC 60250 |
34 |
| DIELECTRIC CONSTANT AT 1MHZ |
kV/mm |
IEC 60250 |
3.8 |
| CTI |
|
IEC 60112 |
450 |
| PHYSICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| DENSITY |
g/cm3 |
ASTM-D792 |
1.53 |
| WATER ABSORPTION (SATURATION) |
% |
ASTM-D570 |
0.5 |
| MOULD SHRINKAGE |
% |
-- |
0.3 |
| MFI |
g/10min |
ASTM-D1238 250/2.16 |
15 |
MOISTURE ABSORPTION
23° C, 50% RH (SATURATION) |
% |
ASTM-D570 |
0.1 |
| MECHANICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| TENSILE YIELD STRENGTH |
MPa |
ASTM-D638 |
140 |
| TENSILE MODULUS |
MPa |
ASTM-D638 |
9000 |
| STRAIN @ BREAK |
% |
ASTM-D638 |
3 |
| FLEXURAL STRENGTH |
MPa |
ASTM-D790 |
180 |
| FLEXURAL MODULUS |
MPa |
ASTM-D790 |
8000 |
| NOTCHED IZOD IMPACT STRENGTH +23°C |
j/m |
ASTM-D256 |
125 |
| THERMAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| HDT AT LOAD 1.8 Mpa |
°C |
ASTM D-648 |
210 |
| HDT AT LOAD 0.45 Mpa |
°C |
ASTM D-648 |
220 |
| G.W.F.I |
°C |
IEC 60695 |
650 |
| G.W.I.T. |
°C |
IEC 60695 |
675 |
| FLAMMABILITY |
mm/min |
FMVSS302 |
10 |
| UL FLAMMABILITY |
-- |
UL 94 3mm |
H.B. |
| MELTING POINT |
°C |
ASTM-D3417 |
226 |
| ELECTRICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| VOLUME RESISTANCE |
Ohmxcm |
IEC 60093 |
>10^15 |
| DIELECTRIC STRENGTH |
kV/mm |
IEC 60250 |
34 |
| DIELECTRIC CONSTANT AT 1MHZ |
kV/mm |
IEC 60250 |
3.8 |
| CTI |
|
IEC 60112 |
450 |
|
The information contained in this website is supplied in good faith. However, it is given purely as an indication. It shall not be construed in any way as formal commitment or warranty on our part. Notably in respect of the eventual infringement of any rights of third parties who may use our products. We remain at your entire disposal for any further information that you may require.