PPC372B73
Release Date: 03/04/2013
73% Mineral Filled Polypropylene for Heavy Density Injection Moulding applications.
| ISO |
|
ASTM |
|
RELATED
DOCUMENTS |
|
| PHYSICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| DENSITY |
g/m3 |
ISO-1183 |
2.1 |
| MOULD SHRINKAGE |
% |
ISO-2577 |
0.8-1.2 |
| MFI |
g/10min |
ISO-1133 230/2.16 |
20 |
| MECHANICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| TENSILE YIELD STRENGTH |
MPa |
ISO-527 |
10 |
| TENSILE MODULUS |
MPa |
ISO-527 |
1700 |
| STRAIN @ BREAK |
% |
ISO-527 |
>10 |
| FLEXURAL STRENGTH |
MPa |
ISO-178 |
20 |
| FLEXURAL MODULUS |
MPa |
ISO-178 |
2200 |
| NOTCHED IZOD IMPACT STRENGTH +23°C |
Kj/m2 |
ISO-180 |
10 |
| PHYSICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| DENSITY |
g/m3 |
ASTM-D792 |
2.1 |
| MOULD SHRINKAGE |
% |
-- |
0.8-1.2 |
| MFI |
g/10min |
ASTM-D1238 230/2.16 |
20 |
| MECHANICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| TENSILE YIELD STRENGTH |
MPa |
ASTM-D638 |
10 |
| TENSILE MODULUS |
MPa |
ASTM-D790 |
1700 |
| STRAIN @ BREAK |
% |
ASTM-D638 |
>10 |
| FLEXURAL STRENGTH |
MPa |
ASTM-D790 |
20 |
| FLEXURAL MODULUS |
MPa |
ASTM-D790 |
2200 |
| NOTCHED IZOD IMPACT STRENGTH +23°C |
j/m |
ASTM-D256 |
95 |
|
The information contained in this website is supplied in good faith. However, it is given purely as an indication. It shall not be construed in any way as formal commitment or warranty on our part. Notably in respect of the eventual infringement of any rights of third parties who may use our products. We remain at your entire disposal for any further information that you may require.