PB847I4
Release Date: 21/06/2009
Polyamide 6 chargé de 20% de fibre de verre et minérale, modifié choc pour des applications de moulage par injection.
| ISO |
|
ASTM |
|
RELATED
DOCUMENTS |
|
| PHYSICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| DENSITY |
g/cm3 |
ISO-1183 |
1.3 |
| MOULD SHRINKAGE |
% |
ISO-2577 |
0.5-0.7 |
| MECHANICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| TENSILE YIELD STRENGTH |
MPa |
ISO-527 |
75 |
| TENSILE MODULUS |
MPa |
ISO-527 |
3200 |
| STRAIN @ BREAK |
% |
ISO-527 |
3.5 |
| FLEXURAL STRENGTH |
MPa |
ISO-178 |
125 |
| FLEXURAL MODULUS |
MPa |
ISO-178 |
3500 |
| NOTCHED IZOD IMPACT STRENGTH +23°C |
Kj/m2 |
ISO-180 |
9 |
| THERMAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| MELTING POINT |
°C |
ISO-11357 |
218 |
| PHYSICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| DENSITY |
g/cm3 |
ASTM-D792 |
1.3 |
| MOULD SHRINKAGE |
% |
-- |
0.5-0.7 |
| MECHANICAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| TENSILE YIELD STRENGTH |
MPa |
ASTM-D638 |
75 |
| TENSILE MODULUS |
MPa |
ASTM-D638 |
3200 |
| STRAIN @ BREAK |
% |
ASTM-D638 |
3.5 |
| FLEXURAL STRENGTH |
MPa |
ASTM-D790 |
125 |
| FLEXURAL MODULUS |
MPa |
ASTM-D790 |
3500 |
| NOTCHED IZOD IMPACT STRENGTH +23°C |
j/m |
ASTM-D256 |
90 |
| THERMAL PROPERTIES |
UNIT |
TEST METHOD |
VALUES |
| MELTING POINT |
°C |
ASTM-D3417 |
218 |
|
Les informations fournies dans ce site Web sont fournies de bonne foi. Cependant elles sont purement indiquatives. Elles ne pourraient pas être considérées comme un engagement formal de notre part Notemment au regard et dfroits d'une tierce personne utilisant nos produits Nous restons à votre disposition pour toute demande complémentaire.