Polyamide 6.6 chargé de 25% de fibre de verre, stabilisé chaleur pour des applications de moulage par injection.

ISO		ASTM		RELATED DOCUMENTS

PHYSICAL PROPERTIES	UNIT	TEST METHOD	VALUES
DENSITY	g/cm³	ISO-1183	1.31
WATER ABSORPTION (SATURATION)	%	ISO-62	6.5
MOISTURE ABSORPTION 23� C, 50% RH (SATURATION)	%	ISO-62	1.9
MOULD SHRINKAGE	%	ISO-2577	0.4-0.8
MECHANICAL PROPERTIES	UNIT	TEST METHOD	VALUES
TENSILE YIELD STRENGTH	MPa	ISO-527	170
TENSILE MODULUS	MPa	ISO-527	8600
STRAIN @ BREAK	%	ISO-527	3.5
FLEXURAL STRENGTH	MPa	ISO-178	260
FLEXURAL MODULUS	MPa	ISO-178	8000
NOTCHED IZOD IMPACT STRENGTH +23�C	Kj/m²	ISO-180	11
ROCKWELL HARDNESS		R scale	122
THERMAL PROPERTIES	UNIT	TEST METHOD	VALUES
HDT AT LOAD 1.8 Mpa	°C	ISO-75	245
HDT AT LOAD 0.45 Mpa	°C	ISO-75	255
FLAMMABILITY	mm/min	FMVSS302	16.5
UL FLAMMABILITY		UL-94 3mm	H.B.
MELTING POINT	°C	ISO-11357	256
MAX TEMP CONTINUOUS USE	°C		120
MAX TEMP SHORT PEAKS OPERATION	°C		240
ELECTRICAL PROPERTIES	UNIT	TEST METHOD	VALUES
SURFACE RESISTANCE	Ohm	IEC 60093	10^12
VOLUME RESISTANCE	Ohm x m	IEC 60093	10^15
DIELECTRIC STRENGTH	kV/mm	IEC 60250	90
DIELECTRIC CONSTANT AT 1MHZ	kV/mm	IEC 60250	3.5

Les informations fournies dans ce site Web sont fournies de bonne foi. Cependant elles sont purement indiquatives. Elles ne pourraient pas être considérées comme un engagement formal de notre part Notemment au regard et dfroits d'une tierce personne utilisant nos produits Nous restons à votre disposition pour toute demande complémentaire.