PM7009/PM7109

Release Date: 03/04/2013

Polyacétal copolymère, stabilisé aux UV pour les applications de moulage par injection. MFI 9.

ISO		ASTM		RELATED DOCUMENTS

PHYSICAL PROPERTIES	UNIT	TEST METHOD	VALUES
DENSITY	g/cm³	ISO-1183	1.41
MOULD SHRINKAGE	%	ISO-2577	1.8-22
MFI	g/10min	ISO-1133 190/2.16	9
MECHANICAL PROPERTIES	UNIT	TEST METHOD	VALUES
TENSILE YIELD STRENGTH	MPa	ISO-527	60
STRAIN @ YIELD			10
TENSILE MODULUS	MPa	ISO-527	2350
STRAIN @ BREAK	%	ISO-527	>30
FLEXURAL STRENGTH	MPa	ISO-178	80
FLEXURAL MODULUS	MPa	ISO-178	2600
NOTCHED IZOD IMPACT STRENGTH +23�C	Kj/m²	ISO-180	8
NOTCHED IZOD IMPACT STRENGTH -30�C	Kj/m²	ISO-180	7
NOTCHED CHARPY IMPACT STRENGTH +23�C	Kj/m²	ISO-179	8.5
NOTCHED CHARPY IMPACT STRENGTH -30�C	Kj/m²	ISO-179	7.8
UN NOTCHED CHARPY IMPACT STRENGTH +23�C	Kj/m²	ISO-179	165
UN NOTCHED CHARPY IMPACT STRENGTH -30�C	Kj/m²	ISO-179	180
ROCKWELL HARDNESS		R scale	82
THERMAL PROPERTIES	UNIT	TEST METHOD	VALUES
HDT AT LOAD 1.8 Mpa	°C	ISO-75	110
HDT AT LOAD 0.45 Mpa	°C	ISO-75	160
FLAMMABILITY	mm/min	FMVSS302	30
UL FLAMMABILITY		UL-94 3mm	H.B.
MELTING POINT	°C	ISO-11357	172
ELECTRICAL PROPERTIES	UNIT	TEST METHOD	VALUES
SURFACE RESISTANCE	Ohm	IEC 60093	10^14
VOLUME RESISTANCE	Ohm x m	IEC 60093	10^16
DIELECTRIC STRENGTH	kV/mm	IEC 60250	24
DIELECTRIC CONSTANT AT 1MHZ	kV/mm	IEC 60250	3.8

Les informations fournies dans ce site Web sont fournies de bonne foi. Cependant elles sont purement indiquatives. Elles ne pourraient pas être considérées comme un engagement formal de notre part Notemment au regard et dfroits d'une tierce personne utilisant nos produits Nous restons à votre disposition pour toute demande complémentaire.